Opis
Conformable polymeric material with stable color pigments. Suitable for full car wrapping (or any other smooth or curved surface).
The thickness of the film (mm): 0.17-0.19mm
The thickness of film with release liner: 0.34-0.35mm
Type of film: High grade polymeric multilayered calendared vinyl film with air release channels
Colors: GLOSSY TIFFANY
Width & Length: Standard roll size – 1.52m*18m
Adhesive: Solvent polyacrylate
Adhesive performance properties: (1mil adhesive on 1mil material, bonded to stainless steel panel)
180°Peel (PSTC-101), 20 minute bond – 2.2 lb/inch, 24 hour bond – 3.5 lb/inch
Release liner: Kraft white silicone-coated, paper with a double-sided polyethylene coating
Storing period (shelf life): 2 years if stored in +10°C to +20°C, relative humidity 50%, in original package, away from direct sunlight, clean and dry place
Avg. indoor life: 4 years when followed rules of application and usage
Avg. outdoor life: 3 years when followed rules of application and use
Application: from +17°C to +25°C, usage from -55°C to +65°C
Dimensional stability: shrinkage less than 4%
Plastification: between 27%-35%
Breaking Strength: 22.7 N/10mm (Average) Test Method: ASTM D3759/D3759M-057.4 N/10mm (Average)
Light Ageing in UV Exposure: Test Method: ASTM D4329-13 Cycle A & ISO 105-A02:1993/Cor.2:2005,
Test result: 5
Exposure cycle: ASTM D4329-13 cycle A,
Lamp type: UVA-3408h UV at (60±2.5)°C BPT, 0.89 W/ (m2•nm)@340nm, 4h condensation at (50±2.5)°C BPT, Exposure duration: 49h
Recommended application tools: Squeegee, buffer, knife, masking tape, heat gun, magnets, gloves, IRR thermometer, IRR heater
Application method: Standard methods for calendered films. No overstretching. Post heating
Post-heating temperature: 110°C flat surfaces, 130°C curves, and overlaps
Cure time: 24 hours above 10°C
Aftercare: PH neutral, Avoid wax or solvents
The images, colors, and finishes on the screen are approximate. For the real representation of the product always check the color swatch.